Chemical composition
Nominal: mid-range where both limits are given, the cap where only a maximum is, balance takes the remainder. Exact specified ranges below.
| Element | Name | Content % | |
|---|---|---|---|
| Main elements6 elements | |||
| Fe | Iron | Bal. | |
| Ni | Nickel | 18 – 19% | |
| Co | Cobalt | 8.5 – 9.5% | |
| Mo | Molybdenum | 4.6 – 5.2% | |
| Ti | Titanium | 0.5 – 0.8% | |
| Al | Aluminium | 0.05 – 0.15% | |
| Element | Name | Content % | |
|---|---|---|---|
| Minor & residual6 elements | |||
| C | Carbon | ≤ 0.03% | |
| Mn | Manganese | ≤ 0.1% | |
| Si | Silicon | ≤ 0.1% | |
| P | Phosphorus | ≤ 0.01% | |
| S | Sulphur | ≤ 0.01% | |
| Cr | Chromium | ≤ 0.5% | |
Mechanical minima by form
Guaranteed values differ by form, size and delivery condition; quotations confirm the specification, form, size and condition.
| Form | Condition | Rm MPa | Rp0.2 MPa | A ≥ % | Other requirements and notes |
|---|---|---|---|---|---|
| Plate, sheet and strip | |||||
| Plate, sheet and strip | Historical AMS6521, grade 300 plate | — | — | — | |
| Several forms | |||||
| Bar, forgings, mechanical tubing and flash-welded rings | AMS6514 default delivery: annealed at 816–927 °C for ≥1 h, air cooled or faster, not aged | — | — | — | Also specified: Hardness ≤ 36 HRC |
| Bar, forgings, mechanical tubing and rings (section <101.60 mm) | Aged at 482±6 °C for 4–6 h, longitudinal | ≥ 1930 (280 ksi) | ≥ 1862 (270 ksi) | ≥ 5 | Also specified: Hardness ≥ 52 HRC |
| Bar, forgings, mechanical tubing and rings (section <101.60 mm) | Aged at 482±6 °C for 4–6 h, transverse | ≥ 1930 (280 ksi) | ≥ 1862 (270 ksi) | ≥ 4 | |
| Bar, forgings, mechanical tubing and rings (section 101.60–254.00 mm) | Aged at 482±6 °C for 4–6 h, longitudinal | ≥ 1896 (275 ksi) | ≥ 1862 (270 ksi) | ≥ 4 | |
| Bar, forgings, mechanical tubing and rings (section 101.60–254.00 mm) | Aged at 482±6 °C for 4–6 h, transverse | ≥ 1896 (275 ksi) | ≥ 1862 (270 ksi) | ≥ 2 | |
| Other | |||||
| Welded joints | AMS6463 welding wire: after welding, solution treated at 816 °C for ≥30 min, then aged at 482 °C for 3–5 h | ≥ 1931 (280 ksi) | ≥ 1862 (270 ksi) | ≥ 3 | |
Where this grade is recommended
Matched in 1 service conditions; ranks and scores computed from the condition-scoring matrix.
| Service condition | Industry | Temperature | Rank | Score |
|---|---|---|---|---|
| Landing gear & forgings | Aerospace | 200 – 315 °C | 1 / 7 | 93 |
Designations & equivalents
| UNS | K93120 |
| W.Nr. (Germany) | 1.6358 |
| EN designation | X2NiCoMo18-9-5 |
| Trade name(s) | Maraging 300 / C300 / Vascomax C300 |
| AMS (SAE aerospace) | 6514 |
Cross-references are common near-equivalents for search and shortlisting; substitution across standards requires clause-by-clause verification. All grades in one cross-reference table →
Applicable standards
4 specifications. Name the standard and its edition on the order.
Guaranteed values and required tests differ between specifications — see Mechanical minima by form for the figures per form.
Frequently asked questions
What is Maraging 300 (18Ni300)?
Maraging 300 (18Ni300) — Maraging steel. The 2000 MPa-class workhorse — landing gear, racing drivetrains, die-casting dies
What is the maximum service temperature of 18Ni300?
Typically about 400 °C; the practical limit depends on media, stress and design life — acceptance per the governing standard.
What is the tensile strength of 18Ni300?
The specified minimum tensile strength is 1930 MPa for the main product form. Minima for other forms and sizes are listed under "Mechanical minima by form" on this page.
Which standards cover 18Ni300?
SAE AMS6514 18Ni300, SAE AMS6463 18Ni300Marage 300, MIL-S-46850D 18Ni, SAE AMS6521 18Ni300
Where is 18Ni300 typically used?
Landing gear & forgings (Aerospace)
In which forms is 18Ni300 available?
Tube, plate, strip, bar, forgings, wire and other forms — sizes and delivery condition confirmed per order, with EN 10204 3.1 / 3.2 certification.
Same series
Download PDF datasheet
This grade’s datasheet as an A4 PDF — for filing, printing or forwarding to colleagues.
Download PDF datasheetSupply & enquiry
Tube & pipeφ1 – 219 × 0.25 – 25 mm
Plate4.76 – 80 mm
Barφ8 – 300 mm
Wire & filler metalsφ0.01 – 8 mmFor this grade we can supply, against your service conditions:
- Tube, plate, strip, bar, forgings, wire and more — with size range and lead time
- Chemistry and mechanical test report (EN 10204 3.1 / 3.2)
- Like-for-like alternatives and selection advice
- Applicable standards and inspection scope
Or email us: info@kochlin.com
Further reading: Alloy 625 Grade 1 vs Grade 2: a heat-treatment condition, not a quality level