Physical properties
| Density | 8.3 | g/cm³ |
| Modulus E | 215 | GPa |
| Thermal conductivity | 13.4 | W/(m·K) |
| Thermal expansion | 12.6 | ×10⁻⁶/K |
| Specific heat | 0.42 | kJ/(kg·K) |
| Resistivity | 1.22 | Ω·mm²/m |
Informative values: they vary with composition, condition and test method. Use the governing standard or measured mill data for pressure and heat-transfer calculations.
Chemical composition
Nominal: mid-range where both limits are given, the cap where only a maximum is, balance takes the remainder. Exact specified ranges below.
| Element | Name | Content % | |
|---|---|---|---|
| Main elements6 elements | |||
| Ni | Nickel | ≥ 44.5% | |
| Cr | Chromium | 20 – 24% | |
| Co | Cobalt | 10 – 15% | |
| Mo | Molybdenum | 8 – 10% | |
| Al | Aluminium | 0.8 – 1.5% | |
| C | Carbon | 0.05 – 0.15% | |
| Element | Name | Content % | |
|---|---|---|---|
| Minor & residual6 elements | |||
| Fe | Iron | ≤ 3% | |
| Ti | Titanium | ≤ 0.6% | |
| B | Boron | ≤ 0.006% | |
| Si | Silicon | ≤ 1% | |
| Mn | Manganese | ≤ 1% | |
| S | Sulphur | ≤ 0.015% | |
Mechanical minima by form
Guaranteed values differ by form, size and delivery condition; quotations confirm the specification, form, size and condition.
| Form | Condition | Rm MPa | Rp0.2 MPa | A ≥ % | Other requirements and notes |
|---|---|---|---|---|---|
| Bar and forgings | |||||
| Bar and rod | Annealed after cold working or after hot working | ≥ 655 (95 ksi) | ≥ 240 (35 ksi) | ≥ 35 | |
| Forgings, flanges, fittings and valve parts | Annealed | ≥ 655 (95 ksi) | ≥ 241 (35 ksi) | ≥ 35 | |
| Plate, sheet and strip | |||||
| Hot-rolled plate | Annealed | ≥ 655 (95 ksi) | ≥ 240 (35 ksi) | ≥ 35 | |
| Tube and pipe | |||||
| Seamless pipe and tube | Annealed after cold or hot working | ≥ 665 (96 ksi) | ≥ 240 (35 ksi) | ≥ 35 | |
| Electric-fusion-welded pipe | Annealed (≥1121 °C) | ≥ 655 (95 ksi) | ≥ 240 (35 ksi) | ≥ 30 | |
| Several forms | |||||
| Long products ≤160 mm and flat products ≤20 mm (EN 10302, 2.4663) | +AT (solution annealed) | ≥ 700 | ≥ 270 | ≥ 35 | Flat products under 3 mm: A five points lower. |
Hardness requirement
Required by the standard, conditionally
| Form and thickness | Hardness max |
|---|---|
| Sheet; strip >0.25–3.2 mm | ≤ 86 HRB |
| Strip 0.13–0.25 mm | ≤ 88 HRB |
Likewise limited to cold-rolled deep-drawing and spinning-quality sheet and strip; ordinary plate, sheet and strip carry NO hardness requirement.
More detail 2
This is a hardness CEILING — deep-drawing material must be soft enough to form — the opposite in kind to the floor carried by age-hardened grades.
Under 1.3 mm the Rockwell B reading is affected by specimen thickness; use superficial Rockwell or Vickers instead.
Creep behaviour
Guidance values (MPa) — Mean values of a scatter band. They are neither an acceptance requirement nor a design allowable stress. Figures in parentheses are long-term extrapolations and less reliable than the tested range.
| Temp °C | Creep strength Rp1.0 (1% plastic strain) | Rupture strength Ru | ||
|---|---|---|---|---|
| 10 000 h | 100 000 h | 10 000 h | 100 000 h | |
| 580 | — | — | — | 230 |
| 590 | — | — | — | 210 |
| 600 | — | — | 260 | 190 |
| 610 | — | — | 240 | 170 |
| 620 | — | — | 220 | 155 |
| 630 | — | — | 200 | 143 |
| 640 | — | — | 185 | 133 |
| 650 | 148 | 97 | 170 | 125 |
| 660 | 135 | 90 | 160 | 119 |
| 670 | 124 | 83 | 150 | 113 |
| 680 | 115 | 77 | 141 | 107 |
| 690 | 107 | 71 | 132 | 101 |
| 700 | 99 | 66 | 123 | 95 |
| 710 | 92 | 61 | 116 | 89 |
| 720 | 85 | 56 | 109 | 83 |
| 730 | 79 | 52 | 102 | 77 |
| 740 | 73 | 48 | 96 | 71 |
| 750 | 68 | 44 | 90 | 65 |
| 760 | 63 | 40 | 84 | 60 |
| 770 | 58 | 37 | 79 | 55 |
| 780 | 53 | 34 | 74 | 51 |
| 790 | 49 | 31 | 69 | 47 |
| 800 | 45 | 28 | 65 | 43 |
| 810 | 41 | 26 | 61 | 39 |
| 820 | 38 | 24 | 57 | 36 |
| 830 | 35 | 22 | 53 | 33 |
| 840 | 32 | 20 | 49 | 30 |
| 850 | 29 | 18 | 45 | 27 |
| 860 | 27 | 16 | 42 | 24 |
| 870 | 25 | 14.5 | 39 | 22 |
| 880 | 23 | 13 | 36 | 20 |
| 890 | 21 | 11.5 | 33 | 18 |
| 900 | 19 | 10 | 30 | 16 |
| 910 | 17 | 8.5 | 27 | 14 |
| 920 | 15.5 | 7 | 24 | 12.5 |
| 930 | 14 | 6 | 22 | 11 |
| 940 | 12.5 | 5 | 20 | 9.5 |
| 950 | 11 | 4 | 18 | 8.5 |
| 960 | 9.5 | 3.2 | 16 | 7.5 |
| 970 | 8.5 | 2.5 | 14.5 | 6.5 |
| 980 | 7.5 | 1.9 | 13 | (5.5) |
| 990 | 6.5 | 1.4 | 11.5 | (5) |
| 1000 | 5.5 | 1 | 10 | (4.5) |
Thermal expansion and elastic modulus
| Temperature range | Mean coefficient ×10⁻⁶/K |
|---|---|
| 20–200 °C | 12.6 |
| 20–300 °C | 13.1 |
| 20–400 °C | 13.6 |
| 20–600 °C | 14 |
| 20–800 °C | 15.4 |
| 20–1000 °C | 16.3 |
Elastic modulus vs temperature
| Temp °C | E GPa |
|---|---|
| 20 | 215 |
| 100 | 210 |
| 200 | 203 |
| 300 | 196 |
| 400 | 189 |
| 500 | 182 |
| 600 | 174 |
| 700 | 167 |
| 800 | 160 |
| 900 | 153 |
| 1000 | 146 |
Grain size
Required by the standard, conditionally
| Form and thickness | ASTM micrograin size | Mean grain section dia. |
|---|---|---|
| Sheet ≤1.3 mm | No. 4.5 or finer | ≤ 0.075 mm |
| Sheet >1.3–6.4 mm | No. 3.5 or finer | ≤ 0.110 mm |
| Strip 0.13–0.25 mm | No. 8 or finer | ≤ 0.022 mm |
| Strip >0.25–3.2 mm | No. 4.5 or finer | ≤ 0.075 mm |
Applies only to COLD-ROLLED DEEP-DRAWING AND SPINNING QUALITY sheet and strip.
More detail 4
If the order does not call for that quality, this table does not apply.
For this product class, grain size and hardness REPLACE the ordinary tensile minima — the tensile minima do not apply to it, and vice versa.
The direction is "or finer" (a maximum grain diameter), the opposite of 800H's "No. 5 or coarser": deep drawing needs fine grain against orange peel, creep needs coarse grain.
Strip over 3.2 mm thick or over 305 mm wide is judged on the sheet rows; under 0.13 mm, testing is not recommended.
Where this grade is recommended
Matched in 5 service conditions; ranks and scores computed from the condition-scoring matrix.
| Service condition | Industry | Temperature | Rank | Score |
|---|---|---|---|---|
| HT boiler & superheater | Power & Nuclear | 450 – 600 °C | 1 / 6 | 93 |
| Hydroprocessing & refinery hot service | Oil & Gas | 250 – 400 °C | 3 / 8 | 88 |
| CSP & molten-salt receivers | Hydrogen & New Energy | 300 – 565 °C | 3 / 4 | 87 |
| Waste-to-energy boilers | Environmental & FGD | 450 – 700 °C | 7 / 8 | 83 |
| Molten salt systems | Power & Nuclear | 290 – 565 °C | 3 / 4 | 82 |
Designations & equivalents
| W.Nr. (Germany) | 2.4663 |
| EN designation | NiCr23Co12Mo |
| Trade name(s) | Inconel 617 / Nicrofer 5520 / Haynes 617 |
| ASTM / AISI | B166 / B167 / B168 / B546 / B564 |
| AMS (SAE aerospace) | 5887 / 5888 / 5889 |
| AWS (welding) | A5.11 ENiCrCoMo-1 |
Cross-references are common near-equivalents for search and shortlisting; substitution across standards requires clause-by-clause verification. All grades in one cross-reference table →
Applicable standards
9 specifications. Name the standard and its edition on the order.
Guaranteed values and required tests differ between specifications — see Mechanical minima by form for the figures per form.
Frequently asked questions
What is Alloy 617 · UNS N06617?
Alloy 617 · UNS N06617 — Ni superalloys. Co-Mo strengthened — gas-turbine transition ducts and 700 °C-class power plant
What is the maximum service temperature of N06617?
Typically about 980 °C; the practical limit depends on media, stress and design life — acceptance per the governing standard.
What is the tensile strength of N06617?
The specified minimum tensile strength is 655 MPa for the main product form. Minima for other forms and sizes are listed under "Mechanical minima by form" on this page.
Which standards cover N06617?
ASTM B166, ASTM B167, ASTM B168, ASTM B546, ASTM B564 (forgings), AMS 5887, AMS 5888, AMS 5889, EN 10302 (creep-resisting steels, nickel and cobalt alloys)
Where is N06617 typically used?
HT boiler & superheater (Power & Nuclear); Hydroprocessing & refinery hot service (Oil & Gas); CSP & molten-salt receivers (Hydrogen & New Energy); Waste-to-energy boilers (Environmental & FGD)
In which forms is N06617 available?
Tube, plate, strip, bar, forgings, wire and other forms — sizes and delivery condition confirmed per order, with EN 10204 3.1 / 3.2 certification.
Same series
Download PDF datasheet
This grade’s datasheet as an A4 PDF — for filing, printing or forwarding to colleagues.
Download PDF datasheetSupply & enquiry
Tube & pipeφ1 – 219 × 0.25 – 25 mm
Plate4.76 – 80 mm
Barφ8 – 300 mm
Wire & filler metalsφ0.01 – 8 mmFor this grade we can supply, against your service conditions:
- Tube, plate, strip, bar, forgings, wire and more — with size range and lead time